Carcass Compound Materials Base on Fluoropolymer for Tissue Engineering in Orthopedics
In this work new type of composite materials for application as coatings for intramedullary implants in the field of orthopaedics and traumatology is offered. Method is based on ability of fluoropolymers to act as biologically inert binding agent and ability of fine-dyspersated hydroxyapatite powders to act as biologically active filling agent providing osteoinduction and osteoconduction processes. Results of investigations of adhesion, elastic and morphometric characteristics of offered composite were presented; chemical composition was determined. Estimation of toxicological properties, locally irritant action and hemolytic activity of offered composites was done according to GOST R ISO 10993. In vivo tests were carried out; it was shown that offered composites didn’t cause any negative tissue reactions and stimulated osteogenesis processes in ectopic bone formation test. Key words: Carcass Compound Materials; fluoropolymers; orthopaedic
Carcass Compound Materials; fluoropolymers; orthopaedic
- There are currently no refbacks.
If you have already registered in Journal A and plan to submit article(s) to Journal B, please click the CATEGORIES, or JOURNALS A-Z on the right side of the "HOME".
We only use the following emails to deal with issues about paper acceptance, payment and submission of electronic versions of our journals to databases:
firstname.lastname@example.org; email@example.com; firstname.lastname@example.org
Copyright © Canadian Research & Development Centre of Sciences and Cultures (CRDCSC)
Address:758, 77e AV, Laval, Quebec, H7V 4A8, Canada
Telephone: 1-514-558 6138